Expanded graphite roll

Product Introduction:

Expanded graphite roll is provided by Shanghai Flaming Century International Co., Ltd.,a major Graphite Products supplier in Minerals, Metals & Materials wholesale industry in China.You can check out the specification of Expanded graphite roll below or get any optional result clicking into the following keywords expanded graphite roll , Expanded graphite roll , FC-1200N , Description , Features , Details and you can check the authentications and testimonials of Expanded graphite roll .

Description:


It is made of high quality natural flake graphite. After a series of special
technics like chemical process, the natural flake is made into the FC-1200N.Since
no binding material and additives is added into the sheet, it keeps all the
excellent performance of natural graphite. It is anti-high temperature, anti-low temperature,corrosion-resistant,anti-aging, lubricated, soft and also good at elasticity,plasticity,
condensibility. It is an ideal material to make flexible graphite shim
and gasket.


Mostly Application Area

1.Die Formed Ring packing Ring

2. Be made into gasket through cutting or diecutting as used in liquid level indicator
gasket and crystallizer gasket.

3.When stick on the surface of metal or non-metal,it can be used to improve the sealing
performance and solve the gas phase problem.

4.Used as packing for spiral wound gasket.



Mostly ParameterUse

Temperature:In oxidizing medium -240~550degree,

In non-oxidizing atmosphere -240~3000degree





Pressure:3(Mpa)PH:0-14


Mostly Capability

Item

I

II

Tolerance of density (g/cm 3)

±0.05

±0.06

Tolerance of thickness ( mm)

±0.03

±0.04

Carbon Content( ％)

99.5

98

Tensile Strength(Mpa)

≥4.5

≥4.5

Compressibility ( ％ )

≥30

≥30

Recovery( ％ )

≥15

≥15

Sulphur Content( PPm )

700

1200

Chlorine Content( PPm )

25

50

Stress relaxation( ％ )

10

10

Ignition Loss( ％ )

0.5

2.0



Sheet Site

FC-1200/N--- ROLLS SITE

Density(g/cm 3 )

Length(m)

Width(mm)

Thickness(mm)

0.8-1.1

30-100

≤1000

0.2-0.8